Edition V22N02 | Year 2017 | Editorial Original Article | Pages 45 to 54

Samaneh Nakhaei , Raha Habib Agahi , Amin Aminian , Masoud Rezaeizadeh

Objective: The aim of the present study was to evaluate color changes and force degradation of orthodontic elastomeric ligatures in different stretching patterns during a 8-weeks period. Methods: Two elastomers with the minimum and two with the maximum color changing, and gray elastomers of two brands (American Orthodontics and Ortho Technology) were selected according to an opinion poll with clinicians and color changes after 4 weeks of intraoral use were evaluated. These elastomers were mounted on special jigs fabricated using a CAD-CAM technique, underwent different stretching patterns and the force was measured in 0, 24 hours, 2, 4 and 8 weeks. During in vivo part of the study, force levels of elastomers were measured after 4 weeks on a material testing machine. Data were analyzed with four-way ANOVA and Tukey post hoc tests. Results: All the elastomers showed color changing but the degree of color stability was significantly different. The mean force degradation was higher in 1-mm stretch groups. After 8 weeks, the average residual force of elastomers was 1.45 ± 0.18 N and the maximum force decay was seen in the elastomers that exhibited the maximum initial force. Conclusion: There is significant relationship between the stretching pattern and the amount of residual force of elastomers. Elastomers with higher initial forces exhibited higher percentages of force loss after 8 weeks. It seems that there is a relationship between initial color and color changing of elastomers.

Color, Elastomers, Orthodontics, Force degradation,

Nakhaei S, Agahi RH, Aminian A, Rezaeizadeh M. Discoloration and force degradation of orthodontic elastomeric ligatures. Dental Press J Orthod. 2017 Mar-Apr;22(2):45-54. DOI: http://dx.doi.org/10.1590/2177-6709.22.2.045-054.oar

Related articles