Corrosion behavior of self-ligating and conventional metal brackets

Admin Dental Press

Edition V19N02 | Year 2014 | Editorial Original Article | Pages 108 to 114

Lúcio Henrique Esmeraldo Gurgel Maia , Hibernon Lopes Filho , Antônio Carlos De Oliveira Ruellas , Mônica Tirre De Souza Araújo , Delmo Santiago Vaitsman

Objective: To test the null hypothesis that the aging process in self-ligating brackets is not higher than in conventional brackets. Methods: Twenty-five conventional (GN-3M/Unitek; GE-GAC; VE-Aditek) and 25 self-ligating (SCs-3M/Unitek; INs-GAC; ECs-Aditek) metal brackets from three manufacturers (n = 150) were submitted to aging process in 0.9% NaCl solution at a constant temperature of 37 ± 1°C for 21 days. The content of nickel, chromium and iron ions in the solution collected at intervals of 7, 14 and 21 days was quantified by atomic absorption spectrophotometry. After the aging process, the brackets were analyzed by scanning electron microscopy (SEM) under 22X and 1,000X magnifications. Results: Comparison of metal release in self-ligating and conventional brackets from the same manufacturer proved that the SCs group released more nickel (p < 0.05) than the GN group after 7 and 14 days, but less chromium (p < 0.05) after 14 days and less iron (p < 0.05) at the three experimental time intervals. The INs group released less iron (p < 0.05) than the GE group after 7 days and less nickel, chromium and iron (p < 0.05) after 14 and 21 days. The ECs group released more nickel, chromium and iron (p < 0.05) than the VE group after 14 days, but released less nickel and chromium (p Corrosion, Orthodontic brackets, Metal,

Related articles